SURFACE PREPARATION

To obtain good adhesion to metallic surface, part shall be cleaned

with solvents to remove dirt, grease, and processing lubricants

used in manufacturing.

Wash one small aera at a time, then dry with a clean cloth before

solvent evaporates to prevent redeposition of oil, wax or other

surface contaminents. To maintain a clean solvant supply, always

pour the solvent on the washing cloth.

MIXING INSTRUCTIONS

Proper mixing and correct proportions are extremely important if

optimum results are to be obtained. Mixing by experienced personnel

at a central location is recommended.

CAUTION: Do not mix accelerator with base compound until ready

to use.

1° Thoroughly stir accelerator in its container until an even

consistancy is obtained.

2° Thoroughly stir base compound in its container until an even

consistancy is obtained.

3° Slowly stir the accelerator into the base compound and thoroughly

mix approximately 7 to 10 minutes. Be sure to scrape the sides and

bottom of the container in order to include all the compound in the

mixture and to assure uniform blending. Scrape mixing paddle

periodically to remove unmixed compound. Slow mixing by hand is

recommanded.

FRACTIONAL USE OF UNIT :

When it is desired to use only part of the kit, after homogeneization,

remove the required quantity.

(§ APPLICATION PROPERTIES).

For all informations, consult the Engeneering Services of

LE JOINT FRANCAIS.

APPLICATION INSTRUCTIONS

Application life is the period of time that the mixed compound

remains at a consistency suitable for application with injection or

extrusion guns. Application life is always based on standard

conditions at 23° C and 50 % relative humidity. For evry 5°C rise

in temperature, application life is reduced approximatetly by half,

and for every 5°C down, it is approximatly doubled. High humidity

at the time of mixing shortens application life.

CURING

The lenght of the cure depends on the ambient temperatureand

relative humidity. The temperature/time relationship is

approximately the same for curing as it is for application life . Low

humidities may extend the cure several times. Cure may hastened

by applying heat up to 50° C. JFM 1675 Class B develops a high

state of cure in 14 days at 23°C.